3003 aluminum rounds introduction

3003 aluminum disc series is the most commonly used aluminum sheet and strip product of aluminum-manganese alloy series. Usually because 3003 aluminum discs have aluminum and manganese elements, so this 3003 aluminum disc product is also usually called rust-proof aluminum plate, rust-proof aluminum skin. However, the ratio of 3003 aluminum round sheet is larger than the conventional 1060 aluminum sheet.

Due to the infusion of aluminum and manganese elements, the strength of 3003 aluminum rounds is higher than that of conventional 1060 aluminum sheet. Therefore, the hardness and strength of 3003 aluminum discs are about 10% higher than 1100 aluminum plate and 1060 aluminum plate. In addition, the solubility, formability, and excellent corrosion resistance of 1060 aluminum sheet. For these reasons, 3003 aluminum rounds for insulation are gradually becoming popular in the market, and more and more people are introducing 3003 aluminum rounds.

We provide you with 3003 aluminum round sheet price quotation and can account for detailed 3003 aluminum round sheet price for you. At the same time, we as a 3003 aluminum rounds wholesale, 3003 aluminum rounds sales, 3003 aluminum rounds manufacturers, the three as one 3003 aluminum rounds manufacturers. We will always adhere to the quality first, service first, to provide our customers with aluminum sheet and strip!

Aluminum Circle 1

Characteristics of 3003 aluminum discs

3003 is an AL-Mn alloy, which is a kind of rust-proof aluminum with wide application. The strength of this alloy is not high (slightly higher than industrial pure aluminum) and cannot be strengthened by heat treatment, so cold working method is used to improve its mechanical properties: high plasticity in annealed state, still good plasticity in semi-cold hardening, low plasticity in cold hardening, good corrosion resistance, good weldability, poor machinability. Uses are mainly used for the requirement of high plasticity and good weldability, low load parts working in liquid or gas medium, such as oil tanks, gasoline or lubricating oil conduits, various liquid containers and other small load parts made by deep drawing: wire is used to make rivets.

3003 aluminum round sheet physical properties

3003 aluminum rounds chemical composition.

Aluminum Al: balance silicon Si: 0.6 copper Cu: 0.05 - 0.2 zinc Zn: 0.10 manganese Mn: 1.0 - 1.5 iron Fe: 0.7 single: 0.05

3003 aluminum round sheet mechanical properties: tensile strength σb (MPa) ) 120-160 conditions yield strength σ0.2 (MPa) ) ≥ 85 specimen size: all wall thickness Note: tube room temperature longitudinal mechanical properties of aluminum sheet and strip gj standard (GB/T 3880-2006), applicable to the unified standard for aluminum alloy sheet and strip materials.

3003 aluminum round sheet melting point.

650-680 ∼

3003 aluminum round sheet hardness.

Strength is about 10% higher than 1100

Density of 3003 aluminum rounds.


Elongation of 3003 aluminum discs.

Since 3003 aluminum rounds have aluminum and manganese elements, 3003 aluminum rounds are much harder than 1060 aluminum sheet and 1100 aluminum sheet in terms of hardness. Therefore, the elongation of 3003 aluminum rounds is generally not as good as 1060 aluminum plate. In general, 3003 aluminum rounds are about 10% harder than 1060.

3003 aluminum round sheet executive standards.

National standard:3003 GB/T 3190-1996ISO:AlMn1Cu ISO 209.1-1989Japanese standard:A3003 JIS H4000-1999 JIS H4100-1999Non-standard:31000 IS 736-2001Russian standard:AMu/1400 FOCT4785-1974EN:EN AW- 3003/AlMn1Cu EN 573-3-1994German Standard:AlMnCu/3.0517 DIM1725-1-1986French Standard:3003(A-M1) NFA50-411 NFA50-451British Standard:3103(N3) BS 1470-1988American Standard:3003/A93003 AA/UNS

3003 aluminum rounds annealing heat treatment process:

1) complete annealing: heating 390 ~ 430 ℃; with the effective thickness of different materials, holding time 30 ~ 120min; 30 ~ 50 ℃ / h speed with the furnace cooled to 300 ℃, and then air-cooled.

2) Rapid annealing: heating 350 ~ 370 ℃; with the effective thickness of different materials, holding time 30 ~ 120min; empty or water cooling.

3) quenching and aging: quenching 500 ~ 510 ℃, air-cooled; artificial aging 95 ~ 105 ℃, 3h, air-cooled; natural aging room temperature 120h